Harris® 0
Harris 0 is a low cost alloy that is suitable for most copper-to-copper or brass joints where close tolerance can be maintained.
Features
- Economical choice for copper brazing
- Copper is self-fluxing
- Alloy flows quickly at brazing temperature so requires close joint tolerance (less than 0.005″)
- Primarily used in manual brazing applications
- Also a suitable for brazing brass
- Operators should avoid over heating the brass and use Stay Silv® white brazing flux
- Not recommended for brazing steel or other ferrous base metals
- Should not use Harris 0 if braze is exposed to sulfur or sulfur compounds in service
- Recommended joint clearance of .002″-.007″
- Conforms to the EU Reach & RoHS directive
Typical Applications
- Copper-to-copper joint brazing
- Brass joint brazing
Technical Specs
- Solidus 1310ºF (710°C)
- Liquidus 1460°F (793°C)
- Brazing Range 1345°F- 1500°F (730°C -816°C)
- AWS A5.8 BCuP-2
- ASME Section IIC SFA 5.8 BCuP-2
- ISO 17672 CuP 181
Download Tech Sheet